- 密度 [g/cm3]: 1.45
- 吸水率 [%]: 0.13
- 缺口沖擊強度: 1.6
- 斷裂伸長率 [%]: 214
- 彎曲強度 [MPa]: 138.0
- 彎曲模量 [MPa]: 8.27
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in3 | ASTM D792 |
| Water Absorption | 0.13 % | 0.13 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 3.17 mm | 0.0020 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 138 MPa | 20000 psi | ASTM D638 |
| Flexural Yield Strength | 214 MPa | 31000 psi | ASTM D790 |
| Flexural Modulus | 8.27 GPa | 1200 ksi | ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm @Thickness 3.17 mm | 3.00 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.25 | 0.25 | |
| Coefficient of Friction, Static | 0.20 | 0.20 | |
| K (wear) Factor | 141 x 10-8 mm3/N-M | 70.0 x 10-10 in3-min/ft-lb-hr | Thrust washer at 2000 PV |
| Limiting Pressure Velocity | 0.701 MPa-m/sec | 20000 psi-ft/min | at 100 FPM, ambient temperature, thrust washer. |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ASTM D648 |