- 密度 [g/cm3]: 1.17
- 缺口沖擊強度: 0.33
- 拉伸強度 [MPa]: 63.0
- 斷裂伸長率 [%]: 99.0
- 彎曲模量 [MPa]: 2.87
- 熱變形溫度 [℃]: 197.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ASTM D792 |
| Density | 1.17 g/cc | 0.0423 lb/in3 | ASTM D792 |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.250 % | 0.250 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Time 86400 sec | 0.0040 - 0.0070 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.011 cm/cm @Time 86400 sec | 0.0080 - 0.011 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 63.0 MPa | 9140 psi | Type I, 5 mm/min; ASTM D638 |
| 64.0 MPa | 9280 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | Type I, 5 mm/min; ASTM D638 |
| 64.0 MPa | 9280 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.2 % | 2.2 % | Type I, 5 mm/min; ASTM D638 |
| 2.4 % | 2.4 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.2 % | 2.2 % | Type I, 5 mm/min; ASTM D638 |
| 2.4 % | 2.4 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.50 GPa | 508 ksi | 1 mm/min; ISO 527 |
| 3.62 GPa | 525 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 97.0 MPa | 14100 psi | ISO 178 |
| 98.0 MPa | 14200 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 99.0 MPa | 14400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.87 GPa | 416 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 3.02 GPa | 438 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.330 J/cm | 0.618 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.92 J/cm | 5.47 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m2 | 1.43 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 17.0 kJ/m2 | 8.09 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 3.00 J @Temperature 23.0 °C | 2.21 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.36 | 0.36 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.32 | 0.32 | ASTM D3702 Modified |
| K (wear) Factor | 14.1 x 10-8 mm3/N-M | 7.00 x 10-10 in3-min/ft-lb-hr | Ring; ASTM D3702 Modified |
| 260 x 10-8 mm3/N-M | 129 x 10-10 in3-min/ft-lb-hr | Washer; ASTM D3702 Modified | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 82.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 45.6 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 125 μm/m-°C @Temperature -30.0 - 30.0 °C | 69.4 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 197 °C | 387 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 200 °C @Thickness 3.20 mm | 392 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 162 °C | 324 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 183 °C @Thickness 3.20 mm | 361 °F @Thickness 0.126 in | unannealed; ASTM D648 | |