- 密度 [g/cm3]: 1.25
- 缺口沖擊強度: 0.94
- 拉伸強度 [MPa]: 177.0
- 斷裂伸長率 [%]: 267
- 彎曲模量 [MPa]: 11.8
- 熱變形溫度 [℃]: 212.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ASTM D792 |
| Density | 1.25 g/cc | 0.0452 lb/in3 | ASTM D792 |
| Moisture Absorption | 0.150 % | 0.150 % | 50% RH, 24 hrs; ASTM D570 |
| 0.230 % | 0.230 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0040 cm/cm @Time 86400 sec | 0.0010 - 0.0040 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.010 cm/cm @Time 86400 sec | 0.0070 - 0.010 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 177 MPa | 25700 psi | 5 mm/min; ISO 527 |
| 182 MPa | 26400 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 177 MPa | 25700 psi | 5 mm/min; ISO 527 |
| 182 MPa | 26400 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 14.77 GPa | 2142 ksi | 1 mm/min; ISO 527 |
| 15.74 GPa | 2283 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 253 MPa | 36700 psi | ISO 178 |
| 266 MPa | 38600 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 267 MPa | 38700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 11.8 GPa | 1710 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 11.96 GPa | 1735 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.940 J/cm | 1.76 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.30 J/cm | 15.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m2 | 4.76 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 51.0 kJ/m2 | 24.3 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C | 5.90 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.48 | 0.48 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.33 | 0.33 | ASTM D3702 Modified |
| K (wear) Factor | 28.2 x 10-8 mm3/N-M | 14.0 x 10-10 in3-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 27.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 15.0 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 81.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 45.0 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 215 °C @Thickness 3.20 mm | 419 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 194 °C | 381 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 200 °C @Thickness 3.20 mm | 392 °F @Thickness 0.126 in | unannealed; ASTM D648 | |