- 密度 [g/cm3]: 1.32
- 缺口沖擊強度: 0.28
- 彎曲模量 [MPa]: 2.61
- 熱變形溫度 [℃]: 159.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ASTM D792 |
| Density | 1.32 g/cc | 0.0477 lb/in3 | ASTM D792 |
| Moisture Absorption | 0.220 % | 0.220 % | 50% RH, 24 hrs; ASTM D570 |
| 0.260 % | 0.260 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec | >= 0.020 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec | 0.020 - 0.040 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 44.0 MPa | 6380 psi | 5 mm/min; ISO 527 |
| 45.0 MPa | 6530 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 3.7 % | 3.7 % | 5 mm/min; ISO 527 |
| 3.9 % | 3.9 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 3.5 % | 3.5 % | 5 mm/min; ISO 527 |
| 3.6 % | 3.6 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.67 GPa | 387 ksi | 1 mm/min; ISO 527 |
| 2.74 GPa | 397 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 73.0 MPa | 10600 psi | ISO 178 |
| 76.0 MPa | 11000 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.61 GPa | 379 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.65 GPa | 384 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.280 J/cm | 0.525 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.29 J/cm | 6.16 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m2 | 0.952 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 18.0 kJ/m2 | 8.57 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 4.00 J @Temperature 23.0 °C | 2.95 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.56 | 0.56 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.59 | 0.59 | ASTM D3702 Modified |
| K (wear) Factor | 26.2 x 10-8 mm3/N-M | 13.0 x 10-10 in3-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 88.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 48.9 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 87.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 48.3 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 159 °C | 318 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 170 °C @Thickness 3.20 mm | 338 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 106 °C @Thickness 3.20 mm | 223 °F @Thickness 0.126 in | unannealed; ASTM D648 | |