- 密度 [g/cm3]: 1.32
- 成型收縮率 [%]: 0.001
- 缺口沖擊強度: 1.06
- 彎曲模量 [MPa]: 8.20
- 熱變形溫度 [℃]: 205.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | DAM; ASTM D792 | ||
| Density | 1.32 g/cc | 0.0477 lb/in3 | DAM; ISO 1183 | ||
| Filler Content | 33 % | 33 % | DAM | ||
| Linear Mold Shrinkage | 0.0010 cm/cm @Thickness 1.60 mm | 0.0010 in/in @Thickness 0.0630 in | Flow; DAM | ||
| 0.0020 cm/cm @Thickness 3.20 mm | 0.0020 in/in @Thickness 0.126 in | Flow; DAM | |||
| 0.0040 cm/cm @Thickness 6.40 mm | 0.0040 in/in @Thickness 0.252 in | Flow; DAM | |||
| 0.0090 cm/cm @Thickness 1.60 mm | 0.0090 in/in @Thickness 0.0630 in | Transverse; DAM | |||
| 0.010 cm/cm @Thickness 3.20 mm | 0.010 in/in @Thickness 0.126 in | Transverse; DAM | |||
| 0.011 cm/cm @Thickness 6.40 mm | 0.011 in/in @Thickness 0.252 in | Transverse; DAM | |||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 2.00 mm | 0.0030 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Thickness 2.00 mm | 0.0090 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 140 MPa @Temperature 23.0 °C | 20300 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 168 MPa @Temperature 23.0 °C | 24400 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Tensile Strength | 165 MPa @Temperature 23.0 °C | 23900 psi @Temperature 73.4 °F | DAM; ASTM D638 | ||
| Elongation at Break | 3.0 % @Temperature 23.0 °C | 3.0 % @Temperature 73.4 °F | DAM; ASTM D638 | ||
| 3.0 % @Temperature 23.0 °C | 3.0 % @Temperature 73.4 °F | DAM; ISO 527 | |||
| 3.2 % @Temperature 23.0 °C | 3.2 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 7.90 GPa @Temperature 23.0 °C | 1150 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 9.50 GPa @Temperature 23.0 °C | 1380 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Strength | 245 MPa @Temperature 23.0 °C | 35500 psi @Temperature 73.4 °F | DAM; ASTM D790 | ||
| Flexural Modulus | 8.20 GPa @Temperature 23.0 °C | 1190 ksi @Temperature 73.4 °F | DAM; ASTM D790 | ||
| 8.20 GPa @Temperature 23.0 °C | 1190 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
| Izod Impact, Notched | 1.06 J/cm @Temperature 23.0 °C | 1.99 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 | ||
| Izod Impact, Unnotched | 10.65 J/cm @Temperature 23.0 °C | 19.95 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D4812 | ||
| Izod Impact, Notched (ISO) | 11.0 kJ/m2 @Temperature -40.0 °C | 5.23 ft-lb/in2 @Temperature -40.0 °F | DAM; ISO 180/1A | ||
| 13.0 kJ/m2 @Temperature 23.0 °C | 6.19 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| Charpy Impact, Notched | 1.20 J/cm2 @Temperature -40.0 °C | 5.71 ft-lb/in2 @Temperature -40.0 °F | DAM; ISO 179/1eA | ||
| 1.30 J/cm2 @Temperature 23.0 °C | 6.19 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 600 V @Temperature 23.0 °C | 600 V @Temperature 73.4 °F | DAM; UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 μm/m-°C @Temperature -40.0 - 23.0 °C | 278 μin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ASTM E 831 | ||
| 500 μm/m-°C @Temperature 23.0 - 55.0 °C | 278 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
| 500 μm/m-°C @Temperature 55.0 - 160 °C | 278 μin/in-°F @Temperature 131 - 320 °F | DAM; ASTM E 831 | |||
| 500 μm/m-°C @Temperature -40.0 - 23.0 °C | 278 μin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | |||
| 500 μm/m-°C @Temperature 23.0 - 55.0 °C | 278 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 500 μm/m-°C @Temperature 55.0 - 160 °C | 278 μin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 83.0 μm/m-°C @Temperature -40.0 - 23.0 °C | 46.1 μin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ASTM E 831 | ||
| 83.0 μm/m-°C @Temperature -40.0 - 23.0 °C | 46.1 μin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | |||
| 113 μm/m-°C @Temperature 23.0 - 55.0 °C | 62.8 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
| 113 μm/m-°C @Temperature 23.0 - 55.0 °C | 62.8 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 158 μm/m-°C @Temperature 55.0 - 160 °C | 87.8 μin/in-°F @Temperature 131 - 320 °F | DAM; ASTM E 831 | |||
| 158 μm/m-°C @Temperature 55.0 - 160 °C | 87.8 μin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| Melting Point | 215 °C | 419 °F | DAM; ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | DAM; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | DAM; ASTM D648 | ||
| 200 °C | 392 °F | DAM; ISO 75-1/-2 | |||
| UL RTI, Electrical | 105 °C @Thickness 0.710 mm | 221 °F @Thickness 0.0280 in | DAM; UL 746B | ||
| 120 °C @Thickness 1.50 mm | 248 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 120 °C @Thickness 3.00 mm | 248 °F @Thickness 0.118 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 120 °C @Thickness 1.50 mm | 248 °F @Thickness 0.0591 in | DAM; UL 746B | ||
| 120 °C @Thickness 3.00 mm | 248 °F @Thickness 0.118 in | DAM; UL 746B | |||
| Flammability, UL94 | HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | DAM; IEC 60695-11-10 | ||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; UL94 | |||
| HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | DAM; UL94 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |||
| Glow Wire Test | 675 °C @Thickness 1.50 mm | 1250 °F @Thickness 0.0591 in | DAM; IEC 60695-2-12 | ||
| 675 °C @Thickness 0.710 mm | 1250 °F @Thickness 0.0280 in | DAM; IEC 60695-2-12 | |||
| 700 °C @Thickness 3.00 mm | 1290 °F @Thickness 0.118 in | DAM; IEC 60695-2-12 | |||
| 700 °C @Thickness 0.710 mm | 1290 °F @Thickness 0.0280 in | DAM; Ignition; IEC 60695-2-13 | |||
| 700 °C @Thickness 1.50 mm | 1290 °F @Thickness 0.0591 in | DAM; Ignition; IEC 60695-2-13 | |||
| 725 °C @Thickness 3.00 mm | 1340 °F @Thickness 0.118 in | DAM; Ignition; IEC 60695-2-13 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 218 °C | 424 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 290 °C | 554 °F | DAM; Optimum | |||
| 280 - 300 °C | 536 - 572 °F | DAM | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.15 % | <= 0.15 % | DAM | ||
| Descriptive Properties | |||||
| Additive | Lubricant | DAM | |||
| Appearance | Black Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | Dimensional Stability, Good | DAM | |||
| Moisture Absorption, Low | DAM | ||||
| Filler | Glass fiber reinforcement | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 612 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA612-GF33< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA612 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass Reinforced Resins | DAM | |||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA612-GF33 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Ultrasonic Weldable | Yes | DAM | |||
| Uses | Appliance Components | DAM | |||
| Automotive Applications | DAM | ||||
| Electrical/Electronic Applications | DAM | ||||
| Industrial Applications | DAM | ||||