- 熔體流動速率 [g/10min]: 2.0
- 密度 [g/cm3]: 1.04
- 吸水率 [%]: 1.8
- 拉伸強度 [MPa]: 30.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in3 | |
| Water Absorption | 1.8 % | 1.8 % | |
| Melt Flow | 2.0 g/10 min @Load 5.00 kg, Temperature 235 °C | 2.0 g/10 min @Load 11.0 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 30.0 MPa @Strain 50.0 % | 4350 psi @Strain 50.0 % | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Tensile Modulus | 0.520 GPa | 75.4 ksi | 1 mm/min |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 183 °C | 361 °F | 10°C/min |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.10 mm | HB @Thickness 0.122 in | ||