- 密度 [g/cm3]: 1.04
- 吸水率 [%]: 1.9
- 彎曲強度 [MPa]: 38.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 - 1.35 g/cc | 0.0376 - 0.0488 lb/in3 | Average value: 1.11 g/cc Grade Count:8 |
| Water Absorption | 1.90 % | 1.90 % | Average value: 1.90 % Grade Count:8 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 38.0 - 47.0 MPa | 5510 - 6820 psi | Average value: 42.5 MPa Grade Count:3 |
| Taber Abrasion, mg/1000 Cycles | 17.0 | 17.0 | Average value: 17.0 Grade Count:3 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 - 3.50e+14 ohm-cm | 1.00e+14 - 3.50e+14 ohm-cm | Average value: 1.68e+14 ohm-cm Grade Count:11 |
| Surface Resistance | 1.00e+14 - 2.40e+14 ohm | 1.00e+14 - 2.40e+14 ohm | Average value: 1.38e+14 ohm Grade Count:11 |
| Dielectric Constant | 3.10 - 3.90 | 3.10 - 3.90 | Average value: 3.50 Grade Count:3 |
| Dielectric Strength | 9.00 - 30.5 kV/mm | 229 - 775 kV/in | Average value: 28.2 kV/mm Grade Count:11 |
| Thermal Properties | Metric | English | Comments |
| Heat of Fusion | 83.7 J/g | 36.0 BTU/lb | Average value: 83.7 J/g Grade Count:3 |
| CTE, linear | 150 μm/m-°C | 83.3 μin/in-°F | Average value: 150 μm/m-°C Grade Count:3 |
| Melting Point | 185 °C | 365 °F | Average value: 185 °C Grade Count:8 |
| Vicat Softening Point | 160 °C | 320 °F | Average value: 160 °C Grade Count:8 |
| Flammability, UL94 | HB - V-2 | HB - V-2 | Grade Count:8 |