- 熔體流動速率 [g/10min]: 11.9
- 密度 [g/cm3]: 1.04
- 拉伸強度 [MPa]: 30.0
- 熱變形溫度 [℃]: 135.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in3 | |
| Melt Flow | 11.9 g/10 min @Load 2.16 kg, Temperature 235 °C | 11.9 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 20 % | 20 % | 50 mm/min |
| Tensile Modulus | 0.525 GPa | 76.1 ksi | 1 mm/min |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | |
| Surface Resistance | 2.00e+12 ohm | 2.00e+12 ohm | |
| Dielectric Strength | 26.0 kV/mm | 660 kV/in | |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 120 μm/m-°C @Temperature 20.0 °C | 66.7 μin/in-°F @Temperature 68.0 °F | |
| Melting Point | 183 °C | 361 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | |
| Vicat Softening Point | 146 °C | 295 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.10 mm | HB @Thickness 0.122 in | ||