- 密度 [g/cm3]: 1.35
- 吸水率 [%]: 1.2
- 缺口沖擊強度: 1.8
- 拉伸強度 [MPa]: 130.0
- 彎曲模量 [MPa]: 5.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in3 | DIN 53479 |
| Water Absorption | 1.2 % | 1.2 % | DIN 53495 |
| Linear Mold Shrinkage | 0.0016 cm/cm | 0.0016 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 130 MPa | 18900 psi | ASTM-D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM-D638 |
| Tensile Modulus | 7.50 GPa | 1090 ksi | ASTM-D790 |
| Flexural Strength | 150 MPa | 21800 psi | ASTM D790 |
| Flexural Modulus | 5.00 GPa | 725 ksi | ASTM-D790 |
| Izod Impact, Notched | 1.80 J/cm @Temperature 23.0 °C | 3.37 ft-lb/in @Temperature 73.4 °F | ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 165 - 175 °C | 329 - 347 °F | |
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | |