- 密度 [g/cm3]: 1.03
- 吸水率 [%]: 1.5
- 缺口沖擊強(qiáng)度: 9.99
- 拉伸強(qiáng)度 [MPa]: 34.0
- 彎曲模量 [MPa]: 0.400
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in3 | DIN 53479 |
| Water Absorption | 1.5 % | 1.5 % | DIN 53495 |
| Linear Mold Shrinkage | 0.0164 cm/cm | 0.0164 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM-D638 |
| Elongation at Break | 300 % | 300 % | ASTM-D638 |
| Flexural Strength | 20.0 MPa | 2900 psi | ASTM D790 |
| Flexural Modulus | 0.400 GPa | 58.0 ksi | ASTM-D790 |
| Izod Impact, Notched | 9.99 J/cm @Temperature 23.0 °C | 18.7 ft-lb/in @Temperature 73.4 °F | ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 175 °C | 347 °F | |
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | |