- 密度 [g/cm3]: 1.02
- 缺口沖擊強度: 5.0
- 拉伸強度 [MPa]: 30.0
- 彎曲模量 [MPa]: 0.450
- 硬度: 80.0
- 熱變形溫度 [℃]: 125.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in3 | DIN 53479 |
| Moisture Absorption at Equilibrium | 0.70 % | 0.70 % | 50%RH; DIN 53714 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 80 | 80 | ASTM-D785 |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM-D638 |
| Elongation at Break | 20 % | 20 % | ASTM-D638 |
| Flexural Strength | 25.0 MPa | 3630 psi | ASTM D790 |
| Flexural Modulus | 0.450 GPa | 65.3 ksi | ASTM-D790 |
| Izod Impact, Notched | 5.00 J/cm @Temperature 23.0 °C | 9.37 ft-lb/in @Temperature 73.4 °F | ASTM-D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | DIN 53482 |
| Dielectric Strength | 55.0 kV/mm | 1400 kV/in | VDE 0303/4 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 165 - 175 °C | 329 - 347 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | |