- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 0.12
- 缺口沖擊強(qiáng)度: 0.78
- 彎曲強(qiáng)度 [MPa]: 41.0
- 彎曲模量 [MPa]: 1.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in3 | ASTM D792 |
| Water Absorption | 0.12 % | 0.12 % | ASTM D570 |
| Linear Mold Shrinkage | 0.017 cm/cm | 0.017 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ATSM D638 |
| Elongation at Break | 20 % | 20 % | ASTM D638 |
| Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
| Flexural Modulus | 1.10 GPa | 160 ksi | ASTM D790 |
| Izod Impact, Notched | 0.780 J/cm | 1.46 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 180 °C | 356 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 °C | 120 °F | ASTM D648 |