- 熔體流動速率 [g/10min]: 5.0
- 密度 [g/cm3]: 1.42
- 吸水率 [%]: 1.0
- 拉伸強度 [MPa]: 52.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in3 | |
| Water Absorption | 1.0 % | 1.0 % | |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 235 °C | 5.0 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | 50 mm/min |
| Elongation at Break | 18 % | 18 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min |
| Tensile Modulus | 3.64 GPa | 528 ksi | 1 mm/min |
| Charpy Impact Unnotched | 8.11 J/cm2 | 38.6 ft-lb/in2 | |
| 7.60 J/cm2 @Temperature -30.0 °C | 36.2 ft-lb/in2 @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 0.420 J/cm2 | 2.00 ft-lb/in2 | |
| 0.350 J/cm2 @Temperature -30.0 °C | 1.67 ft-lb/in2 @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Dissipation Factor | 0.000423 @Frequency 1e+6 Hz | 0.000423 @Frequency 1e+6 Hz | |
| 0.00053 @Frequency 100 Hz | 0.00053 @Frequency 100 Hz | ||
| Thermal Properties | Metric | English | Comments |
| Melting Point | 174 °C | 345 °F | 10°C/min |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.10 mm | HB @Thickness 0.122 in | ||