- 熔體流動速率 [g/10min]: 4.8
- 密度 [g/cm3]: 1.24
- 吸水率 [%]: 1.2
- 彎曲強度 [MPa]: 112.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in3 | |
| Water Absorption | 1.2 % | 1.2 % | |
| Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 235 °C | 4.8 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 112 MPa | 16200 psi | 5 mm/min |
| Elongation at Break | 5.0 % | 5.0 % | 5 mm/min |
| Tensile Modulus | 8.00 GPa | 1160 ksi | 1 mm/min |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 35.5 kV/mm | 902 kV/in | |
| Dissipation Factor | 0.000345 @Frequency 1e+6 Hz | 0.000345 @Frequency 1e+6 Hz | |
| 0.00040 @Frequency 100 Hz | 0.00040 @Frequency 100 Hz | ||
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 174 °C | 345 °F | 10°C/min |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.10 mm | HB @Thickness 0.122 in | ||