- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 0.4
- 缺口沖擊強度: 0.747
- 彎曲模量 [MPa]: 2.59
- 硬度: 103.0
- 熱變形溫度 [℃]: 212.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 - 1.15 g/cc | 0.0412 - 0.0415 lb/in3 | ASTM D792 |
| Water Absorption | 0.40 - 0.50 % | 0.40 - 0.50 % | 24 hrs; ASTM D570 |
| Water Absorption at Saturation | 4.0 - 5.0 % | 4.0 - 5.0 % | ASTM D570 |
| Deformation | 0.70 - 0.80 % | 0.70 - 0.80 % | ASTM D621 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 103 | 103 | ASTM D785 |
| Hardness, Shore D | 78 | 78 | ASTM D2240 |
| Tensile Strength | 65.5 - 75.8 MPa | 9500 - 11000 psi | ASTM D638 |
| Elongation at Break | 45 - 50 % | 45 - 50 % | ASTM D638 |
| Tensile Modulus | 2.59 - 3.28 GPa | 375 - 475 ksi | ASTM D638 |
| Flexural Strength | 96.5 - 110 MPa | 14000 - 16000 psi | ASTM D790 |
| Flexural Modulus | 2.59 - 3.28 GPa | 375 - 475 ksi | ASTM D790 |
| Compressive Strength | 82.7 - 96.5 MPa | 12000 - 14000 psi | ASTM D695 |
| Compressive Modulus | 1.90 - 2.59 GPa | 275 - 375 ksi | ASTM D695 |
| Shear Strength | 55.2 - 62.1 MPa | 8000 - 9000 psi | ASTM D732 |
| Izod Impact, Notched | 0.747 - 0.961 J/cm | 1.40 - 1.80 ft-lb/in | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.12 | 0.12 | ASTM D1894 |
| Coefficient of Friction, Static | 0.25 - 0.35 | 0.25 - 0.35 | ASTM D1894 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.7 @Frequency 60.0 Hz | 3.7 @Frequency 60.0 Hz | ASTM D150 |
| 3.7 @Frequency 1000 Hz | 3.7 @Frequency 1000 Hz | ASTM D150 | |
| 3.7 @Frequency 1.00e+6 Hz | 3.7 @Frequency 1.00e+6 Hz | ASTM D150 | |
| Dielectric Strength | 19.7 - 23.6 kV/mm | 500 - 600 kV/in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 90.0 μm/m-°C | 50.0 μin/in-°F | |
| Melting Point | 227 - 238 °C | 440 - 460 °F | |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous |
| 166 °C | 330 °F | Intermittent | |
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 413 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.7 °C | 179 °F | ASTM D648 |