- 密度 [g/cm3]: 1.15
- 吸水率 [%]: 1.9
- 缺口沖擊強度: 0.534
- 彎曲模量 [MPa]: 2.96
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in3 | ASTM D792 |
| Water Absorption | 1.9 % | 1.9 % | At 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm | 0.015 in/in | 0.125 in; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 75.8 MPa | 11000 psi | ASTM D638 |
| Elongation at Break | 13 % | 13 % | ASTM D638 |
| Flexural Strength | 114 MPa | 16500 psi | ASTM D790 |
| Flexural Modulus | 2.96 GPa | 430 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | 0.125 in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.8 °C | 145 °F | Unannealed; ASTM D648 |