- 密度 [g/cm3]: 1.09
- 缺口沖擊強度: 4.5
- 拉伸強度 [MPa]: 35.0
- 彎曲模量 [MPa]: 0.920
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in3 | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | ISO 527 | ||
| Elongation at Break | >= 50 % | >= 50 % | Nominal; ISO 527 | ||
| Elongation at Yield | 20 % | 20 % | ISO 527 | ||
| Tensile Modulus | 1.20 GPa | 174 ksi | ISO 527 | ||
| Flexural Strength | 30.0 MPa | 4350 psi | ISO 178 | ||
| Flexural Modulus | 0.920 GPa | 133 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 4.50 kJ/m2 @Temperature -40.0 °C | 2.14 ft-lb/in2 @Temperature -40.0 °F | ISO 180 | ||
| 13.0 kJ/m2 @Temperature 23.0 °C | 6.19 ft-lb/in2 @Temperature 73.4 °F | ISO 180 | |||
| Charpy Impact, Notched | 0.700 J/cm2 @Temperature -30.0 °C | 3.33 ft-lb/in2 @Temperature -22.0 °F | ISO 179 | ||
| 1.50 J/cm2 @Temperature 23.0 °C | 7.14 ft-lb/in2 @Temperature 73.4 °F | ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | ISO 3146 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ISO 75 | ||
| Processing Properties | Metric | English | Comments | ||
| Zone 1 | 230 - 250 °C | 446 - 482 °F | Rear | ||
| Zone 2 | 240 - 255 °C | 464 - 491 °F | Middle | ||
| Zone 3 | 230 - 250 °C | 446 - 482 °F | Front | ||
| Zone 4 | 230 - 245 °C | 446 - 473 °F | Head | ||
| Zone 5 | 230 - 245 °C | 446 - 473 °F | Head | ||
| Die Temperature | 230 - 245 °C | 446 - 473 °F | |||
| Melt Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | 0.10 % | 0.10 % | |||
| Descriptive Properties | |||||
| Color | Black | ||||
| Commercial Status | North America | ||||