- 密度 [g/cm3]: 1.23
- 吸水率 [%]: 1.5
- 缺口沖擊強度: 0.641
- 彎曲模量 [MPa]: 4.96
- 熱變形溫度 [℃]: 210.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in3 | ASTM D792 |
| Filler Content | 10 % | 10 % | |
| Water Absorption | 1.5 % | 1.5 % | At 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 110 MPa | 16000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 172 MPa | 25000 psi | ASTM D790 |
| Flexural Modulus | 4.96 GPa | 720 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | 0.125 in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 395 °F | Unannealed; ASTM D648 |