- 密度 [g/cm3]: 1.48
- 吸水率 [%]: 0.9
- 缺口沖擊強度: 0.53
- 彎曲強度 [MPa]: 119.0
- 彎曲模量 [MPa]: 7.00
- 硬度: 121.0
- 熱變形溫度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.90 % | 0.90 % | 24 hour; ISO Test | ||
| 5.7 % | 5.7 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 121 | 121 | ASTM Test | ||
| Tensile Strength at Break | 119 MPa | 17300 psi | 0.2 in/min; ASTM Test | ||
| 49.0 MPa @Temperature 120 °C | 7110 psi @Temperature 248 °F | ASTM Test | |||
| 49.0 MPa @Temperature 120 °C | 7110 psi @Temperature 248 °F | ISO Data | |||
| 58.0 MPa @Temperature 80.0 °C | 8410 psi @Temperature 176 °F | ISO Data | |||
| 58.0 MPa @Temperature 80.0 °C | 8410 psi @Temperature 176 °F | ASTM Test | |||
| 175 MPa @Temperature -40.0 °C | 25400 psi @Temperature -40.0 °F | ASTM Test | |||
| 175 MPa @Temperature -40.0 °C | 25400 psi @Temperature -40.0 °F | ISO Data | |||
| Tensile Strength, Ultimate | 119 MPa | 17300 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 2.6 % | 2.6 % | 0.2 in/min; ASTM Test | ||
| 2.6 % | 2.6 % | 5mm/min; ISO 527 | |||
| 2.9 % @Temperature -40.0 °C | 2.9 % @Temperature -40.0 °F | ISO Data | |||
| 2.9 % @Temperature -40.0 °C | 2.9 % @Temperature -40.0 °F | ASTM Test | |||
| 6.6 % @Temperature 80.0 °C | 6.6 % @Temperature 176 °F | ASTM Test | |||
| 6.6 % @Temperature 80.0 °C | 6.6 % @Temperature 176 °F | ISO Data | |||
| 7.6 % @Temperature 120 °C | 7.6 % @Temperature 248 °F | ASTM Test | |||
| 7.6 % @Temperature 120 °C | 7.6 % @Temperature 248 °F | ISO Data | |||
| Tensile Modulus | 8.29 GPa | 1200 ksi | 1mm/min; ISO 527 | ||
| 2.76 GPa @Temperature 120 °C | 400 ksi @Temperature 248 °F | ISO Data | |||
| 3.31 GPa @Temperature 80.0 °C | 480 ksi @Temperature 176 °F | ISO Data | |||
| 9.21 GPa @Temperature -40.0 °C | 1340 ksi @Temperature -40.0 °F | ISO Data | |||
| Flexural Strength | 186 MPa | 27000 psi | ISO Data | ||
| 200 MPa | 29000 psi | ASTM Test | |||
| Flexural Modulus | 7.00 GPa | 1020 ksi | ISO Data | ||
| 7.60 GPa | 1100 ksi | ASTM Test | |||
| Izod Impact, Notched | 0.530 J/cm @Thickness 3.17 mm | 0.993 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Izod Impact, Notched (ISO) | 5.80 kJ/m2 | 2.76 ft-lb/in2 | ISO Test | ||
| 4.30 kJ/m2 @Temperature -40.0 °C | 2.05 ft-lb/in2 @Temperature -40.0 °F | ISO Test | |||
| Charpy Impact, Notched | 0.400 J/cm2 | 1.90 ft-lb/in2 | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ASTM Test | ||
| 190 °C | 374 °F | ISO 75 | |||
| Descriptive Properties | |||||
| Color | BK-126 | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||