- 熔體流動速率 [g/10min]: 92.25
- 密度 [g/cm3]: 1.23
- 吸水率 [%]: 7.7
- 缺口沖擊強度: 6.0
- 拉伸強度 [MPa]: 130.0
- 彎曲模量 [MPa]: 5.20
- 熱變形溫度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in3 | ISO 1183 | ||
| Water Absorption | 7.7 - 8.3 % | 7.7 - 8.3 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.3 % | 2.3 % | 50% RH | ||
| 2.3 - 2.9 % | 2.3 - 2.9 % | 23°C; 50% RH; ISO 62 | |||
| 7.7 % | 7.7 % | Saturation | |||
| Viscosity Measurement | 140 | 140 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0045 cm/cm | 0.0045 in/in | restricted | ||
| Melt Flow | 92.25 g/10 min @Load 5.00 kg, Temperature 275 °C | 92.25 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 103 MPa | 14900 psi | ASTM D638 | ||
| Tensile Strength, Yield | 130 MPa | 18900 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 | ||
| Elongation at Yield | 3.5 % | 3.5 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 5.80 GPa | 841 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 180 MPa | 26100 psi | at max force; ISO 178 | ||
| Flexural Modulus | 5.20 GPa | 754 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 6.00 kJ/m2 @Temperature 23.0 °C | 2.86 ft-lb/in2 @Temperature 73.4 °F | ISO 180/A | ||
| Charpy Impact Unnotched | 4.50 J/cm2 @Temperature -30.0 °C | 21.4 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | ||
| 4.80 J/cm2 @Temperature -40.0 °C | 22.8 ft-lb/in2 @Temperature -40.0 °F | ASTM D256 | |||
| 5.00 J/cm2 @Temperature 23.0 °C | 23.8 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.700 J/cm2 @Temperature -30.0 °C | 3.33 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.800 J/cm2 @Temperature 23.0 °C | 3.81 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.8 @Frequency 1.00 Hz | 3.8 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.025 @Frequency 1.00e+6 Hz | 0.025 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 550 V | 550 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 0.200 μm/m-°C | 0.111 μin/in-°F | ASTM E831 | ||
| CTE, linear, Parallel to Flow | 0.300 - 0.350 μm/m-°C @Temperature 23.0 - 80.0 °C | 0.167 - 0.194 μin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 0.700 - 0.800 μm/m-°C @Temperature 23.0 - 80.0 °C | 0.389 - 0.444 μin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| Specific Heat Capacity | 1.60 J/g-°C | 0.382 BTU/lb-°F | |||
| Thermal Conductivity | 0.340 W/m-K | 2.36 BTU-in/hr-ft2-°F | DIN 52612 | ||
| Melting Point | 220 °C | 428 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 135 °C | 275 °F | for 50% loss of tensile strength after 20000hr | ||
| 165 °C | 329 °F | for 50% loss of tensile strength after 5000hr | |||
| 200 °C | 392 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1/-2 | ||
| UL RTI, Electrical | 120 °C @Thickness 1.50 mm | 248 °F @Thickness 0.0591 in | 746B | ||
| UL RTI, Mechanical with Impact | 95.0 °C @Thickness 1.50 mm | 203 °F @Thickness 0.0591 in | 746B | ||
| UL RTI, Mechanical without Impact | 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | 746B | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding | ||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Descriptive Properties | |||||
| Commercial Status | Europe and North America | ||||