- 密度 [g/cm3]: 1.48
- 吸水率 [%]: 0.9
- 彎曲強度 [MPa]: 67.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in3 | dry; ISO 1183 | ||
| Water Absorption | 0.90 % | 0.90 % | 24 hour; ISO Test | ||
| 5.7 % | 5.7 % | beginning dry; ISO 62 | |||
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 38.0 MPa @Temperature 120 °C | 5510 psi @Temperature 248 °F | ASTM Test | ||
| 38.0 MPa @Temperature 120 °C | 5510 psi @Temperature 248 °F | ISO Data | |||
| 46.0 MPa @Temperature 80.0 °C | 6670 psi @Temperature 176 °F | ISO Data | |||
| 46.0 MPa @Temperature 80.0 °C | 6670 psi @Temperature 176 °F | ASTM Test | |||
| 153 MPa @Temperature -40.0 °C | 22200 psi @Temperature -40.0 °F | ASTM Test | |||
| 153 MPa @Temperature -40.0 °C | 22200 psi @Temperature -40.0 °F | ISO Data | |||
| Tensile Strength, Ultimate | 67.0 MPa | 9720 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 5.6 % | 5.6 % | 5mm/min; ISO 527 | ||
| 2.6 % @Temperature -40.0 °C | 2.6 % @Temperature -40.0 °F | ISO Data | |||
| 2.6 % @Temperature -40.0 °C | 2.6 % @Temperature -40.0 °F | ASTM Test | |||
| 5.9 % @Temperature 80.0 °C | 5.9 % @Temperature 176 °F | ISO Data | |||
| 5.9 % @Temperature 80.0 °C | 5.9 % @Temperature 176 °F | ASTM Test | |||
| 7.3 % @Temperature 120 °C | 7.3 % @Temperature 248 °F | ASTM Test | |||
| 7.3 % @Temperature 120 °C | 7.3 % @Temperature 248 °F | ISO Data | |||
| Tensile Modulus | 3.90 GPa | 566 ksi | 1mm/min; ISO 527 | ||
| 2.32 GPa @Temperature 120 °C | 336 ksi @Temperature 248 °F | ISO Data | |||
| 3.05 GPa @Temperature 80.0 °C | 442 ksi @Temperature 176 °F | ISO Data | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Descriptive Properties | |||||
| Color | BK-126 | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||