- 密度 [g/cm3]: 1.02
- 拉伸強度 [MPa]: 29.0
- 彎曲模量 [MPa]: 0.575
- 熱變形溫度 [℃]: 55.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in3 | DAM; ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 29.0 MPa @Temperature 23.0 °C | 4210 psi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Tensile Strength, Yield | 29.0 MPa @Temperature 23.0 °C | 4210 psi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Elongation at Break | >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | ||
| 190 % @Temperature 23.0 °C | 190 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | |||
| 220 % @Temperature 23.0 °C | 220 % @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Yield | 220 % @Temperature 23.0 °C | 220 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| Tensile Modulus | 0.475 GPa @Temperature 23.0 °C | 68.9 ksi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Flexural Modulus | 0.575 GPa @Temperature 23.0 °C | 83.4 ksi @Temperature 73.4 °F | DAM; ISO 178 | ||
| Izod Impact, Notched (ISO) | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 180/1A | ||
| Charpy Impact, Notched | 9.50 J/cm2 @Temperature 23.0 °C | 45.2 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 55.0 °C | 131 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 45.0 °C | 113 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 285 °C | 545 °F | DAM; Optimum; Extrusion | |||
| 285 °C | 545 °F | DAM; Optimum; Injection Molding | |||
| 275 - 295 °C | 527 - 563 °F | DAM; Extrusion | |||
| 275 - 295 °C | 527 - 563 °F | DAM; Injection Molding | |||
| Mold Temperature | 60.0 °C | 140 °F | DAM; optimum; Injection Molding | ||
| 40.0 - 80.0 °C | 104 - 176 °F | DAM; Injection Molding | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM; Extrusion | ||
| 80.0 °C | 176 °F | DAM; Injection Molding | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM; Injection Molding | ||
| 4.00 - 6.00 hour | 4.00 - 6.00 hour | DAM; Extrusion | |||
| Moisture Content | <= 0.050 % | <= 0.050 % | DAM; Extrusion | ||
| <= 0.20 % | <= 0.20 % | DAM; Injection Molding | |||
| Descriptive Properties | |||||
| Appearance | Natural Color | DAM | |||
| Features | Chemical Resistance, Good | DAM | |||
| Chemical Resistance, Good | DAM | ||||
| Flexibility, Good | DAM | ||||
| Flexibility, Good | DAM | ||||
| Heat Aging Resistance, Good | DAM | ||||
| Heat Aging Resistance, Good | DAM | ||||
| Impact Modified | DAM | ||||
| Impact Modified | DAM | ||||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66-F< | ISO 11469; DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Toughened Resins | DAM | |||
| Unreinforced Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA66-F | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||