- 密度 [g/cm3]: 1.07
- 缺口沖擊強度: 80.0
- 拉伸強度 [MPa]: 50.0
- 彎曲模量 [MPa]: 1.80
- 熱變形溫度 [℃]: 170.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in3 | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50mm/min; ISO 527 | ||
| Elongation at Break | 45 % | 45 % | 50mm/min, Nominal strain; ISO 527 | ||
| Elongation at Yield | 5.0 % | 5.0 % | 50mm/min; ISO 527 | ||
| Tensile Modulus | 1.90 GPa | 276 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 1.80 GPa | 261 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 80.0 kJ/m2 | 38.1 ft-lb/in2 | ISO Test | ||
| 23.0 kJ/m2 @Temperature -40.0 °C | 10.9 ft-lb/in2 @Temperature -40.0 °F | ISO Test | |||
| Charpy Impact Unnotched | NB | NB | ISO 179 | ||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179 | |||
| Charpy Impact, Notched | 9.00 J/cm2 | 42.8 ft-lb/in2 | ISO 179 | ||
| 2.80 J/cm2 @Temperature -30.0 °C | 13.3 ft-lb/in2 @Temperature -22.0 °F | ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 262 °C | 504 °F | 10 K/min | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ISO 75 | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||