- 密度 [g/cm3]: 1.36
- 缺口沖擊強(qiáng)度: 3.0
- 彎曲強(qiáng)度 [MPa]: 70.0
- 彎曲模量 [MPa]: 4.20
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in3 | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 2.5 % | 2.5 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 4.50 GPa | 653 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 4.20 GPa | 609 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 3.00 kJ/m2 | 1.43 ft-lb/in2 | ISO Test | ||
| Charpy Impact, Notched | 0.250 J/cm2 | 1.19 ft-lb/in2 | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 263 °C | 505 °F | 10 K/min | ||
| 263 °C | 505 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75 | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||