- 熔體流動速率 [g/10min]: 45.2
- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 8.0
- 缺口沖擊強度: 7.0
- 拉伸強度 [MPa]: 50.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in3 | |||
| Density | 1.13 g/cc | 0.0408 lb/in3 | ISO 1183 | ||
| Water Absorption | 8.0 - 9.0 % | 8.0 - 9.0 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.5 - 3.1 % | 2.5 - 3.1 % | 23°C; 50% RH; ISO 62 | ||
| Viscosity Measurement | 190 | 190 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | restricted | ||
| Melt Flow | 45.2 g/10 min @Load 5.00 kg, Temperature 275 °C | 45.2 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Break | >= 50 % | >= 50 % | Nominal, 50mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 20 % | 20 % | 50mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 1.20 GPa | 174 ksi | ISO 527-1/-2 | ||
| Izod Impact, Notched (ISO) | 7.00 kJ/m2 @Temperature -30.0 °C | 3.33 ft-lb/in2 @Temperature -22.0 °F | ISO 180/A | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 180/A | |||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| Charpy Impact, Notched | 2.50 J/cm2 @Temperature 23.0 °C | 11.9 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Tensile Creep Modulus, 1000 hours | 700 MPa @Strain <=0.500 % | 102000 psi @Strain <=0.500 % | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Constant | 5.0 @Frequency 1.00 Hz | 5.0 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.20 @Frequency 1.00e+6 Hz | 0.20 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 1.70 J/g-°C | 0.406 BTU/lb-°F | |||
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft2-°F | DIN 52612 | ||
| Melting Point | 260 °C | 500 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 118 °C | 244 °F | for 50% loss of tensile strength after 20000hr | ||
| 138 °C | 280 °F | for 50% loss of tensile strength after 5000hr | |||
| 200 °C | 392 °F | ||||
| Decomposition Temperature | >= 310 °C | >= 590 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
| Zone 1 | 290 °C | 554 °F | Feed zone | ||
| Zone 2 | 290 °C | 554 °F | Compression | ||
| Zone 3 | 290 °C | 554 °F | Metering-zone | ||
| Zone 4 | 290 °C | 554 °F | Nozzle | ||
| Melt Temperature | 290 °C | 554 °F | Optimal | ||
| 290 - 300 °C | 554 - 572 °F | Injection-molding/Extrusion | |||
| Mold Temperature | 60.0 °C | 140 °F | Optimal | ||
| 40.0 - 80.0 °C | 104 - 176 °F | Injection-molding | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.030 - 0.060 % | 0.030 - 0.060 % | Optimal | ||
| <= 0.15 % | <= 0.15 % | ||||
| Descriptive Properties | |||||
| Commercial Status | Europe | ||||
| Ignition Temperature | >400°C | ASTM D1929 | |||
| Peripheral Screw Speed | < 0.3 m/s | ||||