- 密度 [g/cm3]: 1.58
- 缺口沖擊強度: 0.8
- 彎曲強度 [MPa]: 148.0
- 彎曲模量 [MPa]: 13.4
- 硬度: 115.0
- 熱變形溫度 [℃]: 260.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in3 | |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Ultimate | 148 MPa | 21500 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 211 MPa | 30600 psi | ASTM D790 |
| Flexural Modulus | 13.4 GPa | 1940 ksi | ASTM D790 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.36 J/cm | 6.29 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 - 275 °C | 491 - 527 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 251 °C | 484 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 271 - 285 °C | 520 - 545 °F | Approximate middle barrel temperature range |