- 密度 [g/cm3]: 1.22
- 缺口沖擊強度: 0.59
- 彎曲強度 [MPa]: 72.0
- 彎曲模量 [MPa]: 2.80
- 硬度: 117.0
- 熱變形溫度 [℃]: 192.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in3 | |
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 117 | 117 | ASTM D785 |
| Tensile Strength, Ultimate | 72.0 MPa | 10400 psi | ASTM D638 |
| Elongation at Break | 11 % | 11 % | ASTM D638 |
| Flexural Strength | 97.0 MPa | 14100 psi | ASTM D790 |
| Flexural Modulus | 2.80 GPa | 406 ksi | ASTM D790 |
| Izod Impact, Notched | 0.590 J/cm | 1.11 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| K (wear) Factor | 20.1 x 10-8 mm3/N-M | 10.0 x 10-10 in3-min/ft-lb-hr | K=W/PVT where W=wear (inches^3); P=applied pressure (psi); V=velocity (fpm); T=time (hours). |
| Limiting Pressure Velocity | 0.460 MPa-m/sec | 13100 psi-ft/min | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 - 275 °C | 491 - 527 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 192 °C | 378 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 290 °C | 554 °F | Approximate middle barrel temperature. |