- 密度 [g/cm3]: 1.21
- 缺口沖擊強(qiáng)度: 0.27
- 彎曲強(qiáng)度 [MPa]: 96.0
- 彎曲模量 [MPa]: 4.00
- 硬度: 118.0
- 熱變形溫度 [℃]: 210.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in3 | |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 96.0 MPa | 13900 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 142 MPa | 20600 psi | ASTM D790 |
| Flexural Modulus | 4.00 GPa | 580 ksi | ASTM D790 |
| Izod Impact, Notched | 0.270 J/cm | 0.506 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.59 J/cm | 8.60 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 - 275 °C | 491 - 527 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 271 - 285 °C | 520 - 545 °F | Approximate middle barrel temperature range |