- 密度 [g/cm3]: 1.26
- 缺口沖擊強度: 0.48
- 彎曲強度 [MPa]: 59.0
- 彎曲模量 [MPa]: 2.70
- 硬度: 116.0
- 熱變形溫度 [℃]: 204.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in3 | |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 116 | 116 | ASTM D785 |
| Tensile Strength, Ultimate | 59.0 MPa | 8560 psi | ASTM D638 |
| Elongation at Break | 11 % | 11 % | ASTM D638 |
| Flexural Strength | 92.0 MPa | 13300 psi | ASTM D790 |
| Flexural Modulus | 2.70 GPa | 392 ksi | ASTM D790 |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.60 J/cm | 10.5 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 - 275 °C | 491 - 527 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C | 399 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 290 °C | 554 °F | Approximate middle barrel temperature. |