- 密度 [g/cm3]: 1.23
- 缺口沖擊強度: 0.75
- 彎曲強度 [MPa]: 181.0
- 彎曲模量 [MPa]: 16.9
- 硬度: 120.0
- 熱變形溫度 [℃]: 262.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in3 | |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Ultimate | 181 MPa | 26300 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 291 MPa | 42200 psi | ASTM D790 |
| Flexural Modulus | 16.9 GPa | 2450 ksi | ASTM D790 |
| Izod Impact, Notched | 0.750 J/cm | 1.41 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.25 J/cm | 11.7 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 - 275 °C | 491 - 527 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 262 °C | 504 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 290 °C | 554 °F | Approximate middle barrel temperature. |