- 密度 [g/cm3]: 1.3
- 缺口沖擊強度: 1.28
- 彎曲強度 [MPa]: 112.0
- 彎曲模量 [MPa]: 6.20
- 硬度: 120.0
- 熱變形溫度 [℃]: 229.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in3 | |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Ultimate | 112 MPa | 16200 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Strength | 143 MPa | 20700 psi | ASTM D790 |
| Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D790 |
| Izod Impact, Notched | 1.28 J/cm | 2.40 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.53 J/cm | 14.1 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 - 275 °C | 491 - 527 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 229 °C | 444 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 290 °C | 554 °F | Approximate middle barrel temperature. |