- 密度 [g/cm3]: 1.3
- 缺口沖擊強(qiáng)度: 0.27
- 彎曲強(qiáng)度 [MPa]: 80.0
- 彎曲模量 [MPa]: 4.70
- 硬度: 118.0
- 熱變形溫度 [℃]: 243.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in3 | |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Strength | 134 MPa | 19400 psi | ASTM D790 |
| Flexural Modulus | 4.70 GPa | 682 ksi | ASTM D790 |
| Izod Impact, Notched | 0.270 J/cm | 0.506 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.65 J/cm | 3.09 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 - 275 °C | 491 - 527 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 291 - 302 °C | 556 - 576 °F | Approximate middle barrel temperature range |