- 熔體流動速率 [g/10min]: 8.0
- 密度 [g/cm3]: 1.29
- 吸水率 [%]: 1.9
- 彎曲強度 [MPa]: 140.0
- 熱變形溫度 [℃]: 245.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in3 | |
| Water Absorption | 1.9 % | 1.9 % | |
| Moisture Absorption at Equilibrium | 0.70 % | 0.70 % | Humidity Absorption |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 275 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 527 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 140 MPa | 20300 psi | 5 mm/min |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min |
| Tensile Modulus | 8.80 GPa | 1280 ksi | 1 mm/min |
| Tensile Creep Modulus, 1 hour | 7890 MPa | 1.14e+6 psi | |
| Tensile Creep Modulus, 1000 hours | 5620 MPa | 815000 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 3.0 @Frequency 100 Hz | 3.0 @Frequency 100 Hz | |
| 4.1 @Frequency 1e+6 Hz | 4.1 @Frequency 1e+6 Hz | ||
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 18.0 μm/m-°C @Temperature 20.0 °C | 10.0 μin/in-°F @Temperature 68.0 °F | |
| CTE, linear, Transverse to Flow | 110 μm/m-°C @Temperature 20.0 °C | 61.1 μin/in-°F @Temperature 68.0 °F | |
| Melting Point | 255 °C | 491 °F | 10°C/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | |
| Vicat Softening Point | 195 °C | 383 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||