- 密度 [g/cm3]: 1.39
- 吸水率 [%]: 0.8
- 斷裂伸長(zhǎng)率 [%]: 320
- 彎曲強(qiáng)度 [MPa]: 210.0
- 彎曲模量 [MPa]: 8.80
- 熱變形溫度 [℃]: 260.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in3 | ISO data |
| Water Absorption | 0.80 % | 0.80 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 5.6 % | 5.6 % | in water; 23°C; ISO data |
| Viscosity Measurement | 59 | 59 | Formic Acid Viscosity; ISO data |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ASTM and ISO value |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO Data |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 210 MPa | 30500 psi | Same value from ASTM and ISO tests; 5 mm/min. |
| Elongation at Break | 3.0 % | 3.0 % | Strain at break, ISO, 5 mm/min |
| 3.0 % | 3.0 % | Strain at break, ASTM, 5 mm/min | |
| Tensile Modulus | 10.4 GPa | 1510 ksi | same value from ASTM and ISO test. |
| Flexural Yield Strength | 320 MPa | 46400 psi | ASTM Data |
| Flexural Modulus | 8.80 GPa | 1280 ksi | ISO Value |
| 9.585 GPa | 1390 ksi | ASTM Value | |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Shear Modulus | 3.90 GPa | 566 ksi | calculated |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ISO data |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | ISO data |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 39.0 μm/m-°C @Temperature 20.0 °C | 21.7 μin/in-°F @Temperature 68.0 °F | ASTM data |
| Melting Point | 260 °C | 500 °F | ASTM and ISO test |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | Value for both ASTM and ISO data. |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO data |
| 250 °C | 482 °F | ASTM Data | |
| Flammability, UL94 | HB @Thickness 0.700 mm | HB @Thickness 0.0276 in | |
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 290 °C | 554 °F | See Materials Notes |
| Mold Temperature | 80.0 °C | 176 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |