- 熔體流動速率 [g/10min]: 15.0
- 密度 [g/cm3]: 1.04
- 吸水率 [%]: 2.9
- 拉伸強(qiáng)度 [MPa]: 52.0
- 熱變形溫度 [℃]: 160.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in3 | |
| Water Absorption | 2.9 % | 2.9 % | |
| Moisture Absorption at Equilibrium | 1.2 % | 1.2 % | Humidity Absorption |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 275 °C | 15 g/10 min @Load 4.76 lb, Temperature 527 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 3.4 % | 3.4 % | 50 mm/min |
| Tensile Modulus | 2.60 GPa | 377 ksi | 1 mm/min |
| Tensile Creep Modulus, 1 hour | 2270 MPa | 329000 psi | |
| Tensile Creep Modulus, 1000 hours | 980 MPa | 142000 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 1.9 @Frequency 100 Hz | 1.9 @Frequency 100 Hz | |
| 3.0 @Frequency 1e+6 Hz | 3.0 @Frequency 1e+6 Hz | ||
| Dielectric Strength | 36.0 kV/mm | 914 kV/in | |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 65.0 μm/m-°C @Temperature 20.0 °C | 36.1 μin/in-°F @Temperature 68.0 °F | |
| CTE, linear, Transverse to Flow | 110 μm/m-°C @Temperature 20.0 °C | 61.1 μin/in-°F @Temperature 68.0 °F | |
| Melting Point | 255 °C | 491 °F | 10°C/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||