- 密度 [g/cm3]: 1.187
- 吸水率 [%]: 0.8
- 彎曲強度 [MPa]: 200.0
- 彎曲模量 [MPa]: 8.80
- 熱變形溫度 [℃]: 260.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.187 g/cc | 0.04288 lb/in3 | Melt Density |
| 1.39 g/cc | 0.0502 lb/in3 | ISO data | |
| Water Absorption | 0.80 % | 0.80 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 5.6 % | 5.6 % | in water; 23°C; ISO data |
| Viscosity Measurement | 59 | 59 | Formic Acid Viscosity; ISO data |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ASTM and ISO value |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO Data |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 200 MPa | 29000 psi | ASTM value at 5mm/min. |
| 202 MPa | 29300 psi | ISO value at 5mm/min. | |
| Elongation at Break | 3.0 % | 3.0 % | Strain at break, ISO, 5 mm/min |
| 3.0 % | 3.0 % | Strain at break, ASTM, 5 mm/min | |
| Tensile Modulus | 10.4 GPa | 1510 ksi | ISO test |
| Flexural Modulus | 8.80 GPa | 1280 ksi | ISO Value |
| 9.69 GPa | 1410 ksi | ASTM Value | |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Shear Modulus | 3.90 GPa | 566 ksi | calculated |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | ISO data |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 23.0 μm/m-°C @Temperature 20.0 °C | 12.8 μin/in-°F @Temperature 68.0 °F | ISO data |
| CTE, linear, Transverse to Flow | 70.0 μm/m-°C @Temperature 20.0 °C | 38.9 μin/in-°F @Temperature 68.0 °F | ISO data |
| Specific Heat Capacity | 2.35 J/g-°C | 0.562 BTU/lb-°F | Melt value |
| Thermal Conductivity | 0.331 W/m-K | 2.30 BTU-in/hr-ft2-°F | Melt |
| Melting Point | 260 °C | 500 °F | ASTM and ISO test |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ISO data |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO data |
| 251 °C | 484 °F | ASTM Data | |
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | |
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 290 °C | 554 °F | See Materials Notes |
| Mold Temperature | 80.0 °C | 176 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |