- 密度 [g/cm3]: 1.33
- 缺口沖擊強度: 2.19
- 拉伸強度 [MPa]: 148.2
- 彎曲模量 [MPa]: 7.24
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in3 | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 148.2 MPa | 21490 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Modulus | 7.24 GPa | 1050 ksi | ASTM D790 |
| Izod Impact, Notched | 2.19 J/cm @Thickness 3.17 mm | 4.10 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 254 °C | 490 °F | |
| Middle Barrel Temperature | 268 °C | 515 °F | |
| Front Barrel Temperature | 285 °C | 545 °F | |
| Nozzle Temperature | 266 - 282 °C | 510 - 540 °F | |
| Melt Temperature | 271 - 293 °C | 520 - 560 °F | |
| Mold Temperature | 26.7 - 93.3 °C | 80.0 - 200 °F | |
| Drying Temperature | 71.1 °C | 160 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 68.9 MPa | 10000 psi | |
| Back Pressure | 0.0689 - 0.689 MPa | 10.0 - 100 psi | |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | |