- 吸水率 [%]: 2.9
- 拉伸強度 [MPa]: 50.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Absorption | 2.9 - 3.1 % @Temperature 23.0 °C | 2.9 - 3.1 % @Temperature 73.4 °F | 50% r.h.; ISO 62 |
| Water Absorption at Saturation | 8.0 - 9.0 % @Time 82800 sec | 8.0 - 9.0 % @Time 23.0 hour | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 5 [mm/min], Test Speed 50 [mm/min]; ISO 527-1/2 |
| 25.0 MPa @Temperature 115 - 145 °C, Time 1.80e+7 sec | 3630 psi @Temperature 239 - 293 °F, Time 5000 hour | 5 [mm/min], 50% Loss of Tensile Strength; ICE 216 | |
| 25.0 MPa @Temperature 100 - 120 °C, Time 7.20e+7 sec | 3630 psi @Temperature 212 - 248 °F, Time 20000 hour | 5 [mm/min], 50% Loss of Tensile Strength; ICE 216 | |
| Elongation at Break | >= 50 % | >= 50 % | 5 [mm/min]; ISO 527-1/2 |
| Tensile Modulus | 1.10 GPa | 160 ksi | 1[mm/min]; ISO 527-1/2 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU |
| Charpy Impact, Notched | 1.30 J/cm2 @Temperature 23.0 °C | 6.19 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 262 °C | 504 °F | ISO 11357-1/3 |