- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 0.5
- 缺口沖擊強度: 0.37
- 斷裂伸長率 [%]: 65.5
- 彎曲強度 [MPa]: 48.3
- 彎曲模量 [MPa]: 1.72
- 熱變形溫度 [℃]: 188.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 - 1.99 g/cc | 0.0408 - 0.0719 lb/in3 | Average value: 1.34 g/cc Grade Count:20 |
| Filler Content | 5.00 - 20.0 % | 5.00 - 20.0 % | Average value: 11.1 % Grade Count:10 |
| Water Absorption | 0.500 - 1.50 % | 0.500 - 1.50 % | Average value: 1.06 % Grade Count:7 |
| Linear Mold Shrinkage | 0.00150 - 0.0240 cm/cm | 0.00150 - 0.0240 in/in | Average value: 0.00977 cm/cm Grade Count:19 |
| Linear Mold Shrinkage, Transverse | 0.00400 - 0.0180 cm/cm | 0.00400 - 0.0180 in/in | Average value: 0.0126 cm/cm Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 48.3 - 159 MPa | 7000 - 23100 psi | Average value: 90.4 MPa Grade Count:18 |
| Elongation at Break | 1.00 - 12.0 % | 1.00 - 12.0 % | Average value: 6.16 % Grade Count:19 |
| Modulus of Elasticity | 2.34 - 7.93 GPa | 340 - 1150 ksi | Average value: 4.37 GPa Grade Count:18 |
| Flexural Yield Strength | 65.5 - 255 MPa | 9500 - 37000 psi | Average value: 138 MPa Grade Count:19 |
| Flexural Modulus | 1.72 - 10.3 GPa | 250 - 1490 ksi | Average value: 4.61 GPa Grade Count:19 |
| Izod Impact, Notched | 0.370 - 1.87 J/cm | 0.693 - 3.50 ft-lb/in | Average value: 0.799 J/cm Grade Count:19 |
| Izod Impact, Unnotched | 4.81 - 10.7 J/cm | 9.00 - 20.0 ft-lb/in | Average value: 8.33 J/cm Grade Count:15 |
| K (wear) Factor | 10100 x 10-8 mm3/N-M | 5000 x 10-10 in3-min/ft-lb-hr | Average value: 10100 x 10-8 mm3/N-M Grade Count:3 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00 - 10000 ohm-cm | 1.00 - 10000 ohm-cm | Average value: 810 ohm-cm Grade Count:19 |
| Surface Resistance | 1.00 - 1.00e+6 ohm | 1.00 - 1.00e+6 ohm | Average value: 312000 ohm Grade Count:14 |
| Static Decay | 0.100 - 2.00 sec | 0.100 - 2.00 sec | Average value: 1.72 sec Grade Count:12 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 188 - 243 °C | 370 - 469 °F | Average value: 226 °C Grade Count:6 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.1 - 249 °C | 160 - 480 °F | Average value: 165 °C Grade Count:10 |
| Flammability, UL94 | HB | HB | Grade Count:7 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 70.0 - 293 °C | 158 - 560 °F | Average value: 181 °C Grade Count:6 |
| Melt Temperature | 252 - 320 °C | 485 - 608 °F | Average value: 290 °C Grade Count:12 |
| Mold Temperature | 54.4 - 107 °C | 130 - 225 °F | Average value: 87.8 °C Grade Count:15 |
| Drying Temperature | 70.0 - 121 °C | 158 - 250 °F | Average value: 86.2 °C Grade Count:11 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.75 hour Grade Count:8 |
| Moisture Content | 0.0200 - 0.200 % | 0.0200 - 0.200 % | Average value: 0.176 % Grade Count:9 |
| Dew Point | -30.0 - -28.9 °C | -22.0 - -20.0 °F | Average value: -29.6 °C Grade Count:3 |
| Injection Pressure | 68.9 - 138 MPa | 10000 - 20000 psi | Average value: 90.9 MPa Grade Count:11 |