- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 0.5
- 缺口沖擊強度: 0.374
- 拉伸強度 [MPa]: 55.0
- 斷裂伸長率 [%]: 82.7
- 彎曲強度 [MPa]: 49.6
- 彎曲模量 [MPa]: 2.76
- 硬度: 98.0
- 熱變形溫度 [℃]: 100.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 - 1.51 g/cc | 0.0419 - 0.0546 lb/in3 | Average value: 1.38 g/cc Grade Count:16 |
| Filler Content | 20.0 - 40.0 % | 20.0 - 40.0 % | Average value: 33.3 % Grade Count:3 |
| Water Absorption | 0.500 - 2.60 % | 0.500 - 2.60 % | Average value: 1.03 % Grade Count:6 |
| Moisture Absorption at Equilibrium | 1.10 - 2.00 % | 1.10 - 2.00 % | Average value: 1.70 % Grade Count:3 |
| Linear Mold Shrinkage | 0.00500 - 0.0220 cm/cm | 0.00500 - 0.0220 in/in | Average value: 0.0108 cm/cm Grade Count:15 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00900 - 0.0170 cm/cm | 0.00900 - 0.0170 in/in | Average value: 0.0127 cm/cm Grade Count:3 |
| Linear Mold Shrinkage, Transverse | 0.0137 - 0.0180 cm/cm | 0.0137 - 0.0180 in/in | Average value: 0.0146 cm/cm Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 98.0 - 121 | 98.0 - 121 | Average value: 116 Grade Count:8 |
| Tensile Strength, Ultimate | 49.6 - 110 MPa | 7200 - 16000 psi | Average value: 71.1 MPa Grade Count:12 |
| Tensile Strength, Yield | 55.0 - 91.0 MPa | 7980 - 13200 psi | Average value: 72.3 MPa Grade Count:4 |
| Elongation at Break | 3.00 - 21.0 % | 3.00 - 21.0 % | Average value: 9.54 % Grade Count:13 |
| Elongation at Yield | 2.50 - 16.0 % | 2.50 - 16.0 % | Average value: 7.13 % Grade Count:3 |
| Modulus of Elasticity | 2.45 - 11.0 GPa | 355 - 1600 ksi | Average value: 5.41 GPa Grade Count:8 |
| Flexural Yield Strength | 82.7 - 245 MPa | 12000 - 35500 psi | Average value: 126 MPa Grade Count:14 |
| Flexural Modulus | 2.76 - 9.00 GPa | 400 - 1310 ksi | Average value: 5.00 GPa Grade Count:14 |
| Izod Impact, Notched | 0.374 - 1.07 J/cm | 0.700 - 2.00 ft-lb/in | Average value: 0.807 J/cm Grade Count:10 |
| Izod Impact, Unnotched | 3.74 J/cm - NB | 7.00 ft-lb/in - NB | Average value: 6.65 J/cm Grade Count:9 |
| Izod Impact, Notched (ISO) | 9.00 - 12.5 kJ/m2 | 4.28 - 5.95 ft-lb/in2 | Average value: 10.5 kJ/m2 Grade Count:3 |
| 8.00 - 8.00 kJ/m2 @Temperature -30.0 - -30.0 °C | 3.81 - 3.81 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 8.00 kJ/m2 Grade Count:1 | |
| Charpy Impact Unnotched | 2.50 - 2.50 J/cm2 @Temperature -20.0 - -20.0 °C | 11.9 - 11.9 ft-lb/in2 @Temperature -4.00 - -4.00 °F | Average value: 2.50 J/cm2 Grade Count:1 |
| Charpy Impact, Notched | 0.100 - 0.100 J/cm2 @Temperature -20.0 - -20.0 °C | 0.476 - 0.476 ft-lb/in2 @Temperature -4.00 - -4.00 °F | Average value: 0.100 J/cm2 Grade Count:1 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+13 - 7.70e+15 ohm-cm | 1.00e+13 - 7.70e+15 ohm-cm | Average value: 1.37e+15 ohm-cm Grade Count:8 |
| Surface Resistance | 1.00e+12 - 1.00e+13 ohm | 1.00e+12 - 1.00e+13 ohm | Average value: 7.00e+12 ohm Grade Count:3 |
| Dielectric Strength | 15.0 - 90.0 kV/mm | 380 - 2290 kV/in | Average value: 33.0 kV/mm Grade Count:5 |
| Comparative Tracking Index | 500 - 600 V | 500 - 600 V | Average value: 550 V Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 7.20 - 113 μm/m-°C | 4.00 - 62.8 μin/in-°F | Average value: 55.8 μm/m-°C Grade Count:4 |
| Melting Point | 249 - 275 °C | 480 - 527 °F | Average value: 260 °C Grade Count:9 |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 - 248 °C | 212 - 478 °F | Average value: 211 °C Grade Count:12 |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 - 220 °C | 165 - 428 °F | Average value: 131 °C Grade Count:15 |
| Vicat Softening Point | 140 - 260 °C | 284 - 500 °F | Average value: 213 °C Grade Count:3 |
| Flammability, UL94 | HB | HB | Grade Count:9 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 270 - 300 °C | 518 - 572 °F | Average value: 287 °C Grade Count:8 |
| Melt Temperature | 280 - 310 °C | 536 - 590 °F | Average value: 299 °C Grade Count:3 |
| Mold Temperature | 65.6 - 120 °C | 150 - 248 °F | Average value: 90.5 °C Grade Count:7 |
| Drying Temperature | 75.0 - 105 °C | 167 - 221 °F | Average value: 87.9 °C Grade Count:4 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.33 hour Grade Count:3 |
| Injection Pressure | 70.0 - 124 MPa | 10200 - 18000 psi | Average value: 109 MPa Grade Count:4 |