- 密度 [g/cm3]: 1.33
- 吸水率 [%]: 1.7
- 缺口沖擊強(qiáng)度: 0.961
- 拉伸強(qiáng)度 [MPa]: 241.0
- 彎曲模量 [MPa]: 22.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in3 | ASTM D792 |
| Water Absorption | 1.7 % @Time 86400 sec | 1.7 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0012 cm/cm @Thickness 3.17 mm | 0.0012 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 241 MPa | 35000 psi | ASTM D638 |
| Elongation at Break | 1.7 % | 1.7 % | ASTM D638 |
| Flexural Strength | 393 MPa | 57000 psi | ASTM D790 |
| Flexural Modulus | 22.1 GPa | 3200 ksi | ASTM D790 |
| Izod Impact, Notched | 0.961 J/cm @Thickness 3.17 mm | 1.80 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 10 ohm-cm | 10 ohm-cm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 18.0 μm/m-°C | 10.0 μin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 282 °C | 540 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | |