- 密度 [g/cm3]: 1.35
- 吸水率 [%]: 1.9
- 缺口沖擊強度: 0.801
- 拉伸強度 [MPa]: 276.0
- 彎曲模量 [MPa]: 26.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in3 | ASTM D792 |
| Water Absorption | 1.9 % @Time 86400 sec | 1.9 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0015 cm/cm @Thickness 3.17 mm | 0.0015 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 276 MPa | 40000 psi | ASTM D638 |
| Elongation at Break | 1.5 % | 1.5 % | ASTM D638 |
| Flexural Strength | 434 MPa | 63000 psi | ASTM D790 |
| Flexural Modulus | 26.9 GPa | 3900 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Thickness 3.17 mm | 1.50 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 10 ohm-cm | 10 ohm-cm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 19.8 μm/m-°C | 11.0 μin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | |