- 密度 [g/cm3]: 1.43
- 吸水率 [%]: 1.5
- 缺口沖擊強度: 0.961
- 拉伸強度 [MPa]: 207.0
- 彎曲模量 [MPa]: 8.96
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in3 | ASTM D792 |
| Water Absorption | 1.5 % @Time 86400 sec | 1.5 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Thickness 3.17 mm | 0.0060 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 207 MPa | 30000 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 255 MPa | 37000 psi | ASTM D790 |
| Flexural Modulus | 8.96 GPa | 1300 ksi | ASTM D790 |
| Izod Impact, Notched | 0.961 J/cm @Thickness 3.17 mm | 1.80 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 23.6 kV/mm | 600 kV/in | Method A (Short-Time); ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 18.0 μm/m-°C | 10.0 μin/in-°F | ASTM D696 |
| Melting Point | 295 °C | 563 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 291 °C | 555 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | |