- 密度 [g/cm3]: 1.18
- 吸水率 [%]: 13.0
- 拉伸強(qiáng)度 [MPa]: 100.0
- 熱變形溫度 [℃]: 280.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in3 | ISO 1183 | ||
| Water Absorption | 13 % | 13 % | Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 3.7 % | 3.7 % | Humidity Absorption; Sim. to ISO 62 | ||
| Viscosity Test | 185 cm3/g | 185 cm3/g | Viscosity Number | ||
| Linear Mold Shrinkage, Flow | 0.020 cm/cm | 0.020 in/in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.020 cm/cm | 0.020 in/in | Normal; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 100 MPa | 14500 psi | ISO 527-1/-2 | ||
| Elongation at Break | 40 % | 40 % | ISO 527-1/-2 | ||
| Elongation at Yield | 10 % | 10 % | ISO 527-1/-2 | ||
| Tensile Modulus | 3.30 GPa | 479 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.900 J/cm2 @Temperature -30.0 °C | 4.28 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.20 J/cm2 @Temperature 23.0 °C | 5.71 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| >= 600 V | >= 600 V | PLC 0; UL 746A | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 80.0 μm/m-°C @Temperature 20.0 °C | 44.4 μin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 100 μm/m-°C @Temperature 20.0 °C | 55.6 μin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| Melting Point | 295 °C | 563 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 280 °C | 536 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 290 °C | 554 °F | 50°C/h 50N; ISO 306 | ||
| Glass Transition Temp, Tg | 75.0 °C | 167 °F | Glass Transition Temperature (10°C/min); ISO 11357-1/-2 | ||
| UL RTI, Electrical | 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL746B | ||
| 130 °C @Thickness 0.750 mm | 266 °F @Thickness 0.0295 in | UL746B | |||
| Flammability, UL94 | V-2 @Thickness 0.750 mm | V-2 @Thickness 0.0295 in | IEC 60695-11-10 | ||
| V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | IEC 60695-11-10 | |||
| Descriptive Properties | |||||
| Heat Stabilized or Stable to Heat | Yes | ||||
| Injection Molding | Yes | ||||
| Lubricants | Yes | ||||
| Release Agent | Yes | ||||
| Without Fillers | Yes | ||||