- 密度 [g/cm3]: 1.18
- 吸水率 [%]: 13.0
- 拉伸強度 [MPa]: 55.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in3 | (DAM); ISO 1183 | ||
| Water Absorption | 13 % | 13 % | DAM; Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 3.7 % | 3.7 % | Humidity Absorption (DAM); Sim. to ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.020 cm/cm | 0.020 in/in | DAM; ISO 294-4 | ||
| 0.020 cm/cm | 0.020 in/in | DAM; ISO 294-4 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ISO 527-1/-2 | ||
| Elongation at Break | >= 50 % | >= 50 % | ISO 527-1/-2 | ||
| Elongation at Yield | 20 % | 20 % | ISO 527-1/-2 | ||
| Tensile Modulus | 1.00 GPa | 145 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.20 J/cm2 @Temperature -30.0 °C | 5.71 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| 4.50 J/cm2 @Temperature 23.0 °C | 21.4 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Tensile Creep Modulus, 1000 hours | 500 MPa | 72500 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| >= 600 V | >= 600 V | PLC 0; UL 746A | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 295 °C | 563 °F | 10°C/min (DAM); ISO 11357-1/-3 | ||
| UL RTI, Electrical | 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL746B | ||
| 130 °C @Thickness 0.750 mm | 266 °F @Thickness 0.0295 in | UL746B | |||
| Descriptive Properties | |||||
| Heat Stabilized or Stable to Heat | Yes | ||||
| Injection Molding | Yes | ||||
| Lubricants | Yes | ||||
| Release Agent | Yes | ||||
| Without Fillers | Yes | ||||