- 密度 [g/cm3]: 1.82
- 吸水率 [%]: 4.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.82 g/cc | 0.0658 lb/in3 | (DAM); ISO 1183 | ||
| Water Absorption | 4.5 % | 4.5 % | DAM; Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.2 % | 1.2 % | Humidity Absorption (DAM); Sim. to ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | DAM; ISO 294-4 | ||
| 0.0090 cm/cm | 0.0090 in/in | DAM; ISO 294-4 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527-1/-2 | ||
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 12.0 GPa | 1740 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 5.00 J/cm2 @Temperature -30.0 °C | 23.8 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | ||
| 7.50 J/cm2 @Temperature 23.0 °C | 35.7 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.30 J/cm2 @Temperature -30.0 °C | 6.19 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.50 J/cm2 @Temperature 23.0 °C | 7.14 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Tensile Creep Modulus, 1000 hours | 12000 MPa | 1.74e+6 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | ||
| Dielectric Constant | 4.5 @Frequency 1e+6 Hz | 4.5 @Frequency 1e+6 Hz | IEC 60250 | ||
| 12 @Frequency 100 Hz | 12 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0070 @Frequency 1e+6 Hz | 0.0070 @Frequency 1e+6 Hz | IEC 60250 | ||
| 0.033 @Frequency 100 Hz | 0.033 @Frequency 100 Hz | IEC 60250 | |||
| Comparative Tracking Index | 250 - 399 V | 250 - 399 V | PLC 2; UL 746A | ||
| 325 V | 325 V | IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 295 °C | 563 °F | 10°C/min (DAM); ISO 11357-1/-3 | ||
| UL RTI, Electrical | 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | UL746B | ||
| 140 °C @Thickness 0.750 mm | 284 °F @Thickness 0.0295 in | UL746B | |||
| UL RTI, Mechanical with Impact | 110 °C @Thickness 0.750 mm | 230 °F @Thickness 0.0295 in | UL746B | ||
| 125 °C @Thickness 1.50 mm | 257 °F @Thickness 0.0591 in | UL746B | |||
| UL RTI, Mechanical without Impact | 120 °C @Thickness 0.750 mm | 248 °F @Thickness 0.0295 in | UL746B | ||
| 125 °C @Thickness 1.50 mm | 257 °F @Thickness 0.0591 in | UL746B | |||
| Descriptive Properties | |||||
| Flame Retardant | Yes | ||||
| Flame Retarding Agent | Yes | ||||
| Heat Stabilized or Stable to Heat | Yes | ||||
| Injection Molding | Yes | ||||
| Lubricants | Yes | ||||
| Platable | Yes | ||||
| Release Agent | Yes | ||||
| With Fillers | Yes | ||||