- 密度 [g/cm3]: 1.68
- 吸水率 [%]: 5.9
- 熱變形溫度 [℃]: 290.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.68 g/cc | 0.0607 lb/in3 | ISO 1183 | ||
| Water Absorption | 5.9 % | 5.9 % | Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | Humidity Absorption; Sim. to ISO 62 | ||
| Viscosity Test | 145 cm3/g | 145 cm3/g | Viscosity Number | ||
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | Normal; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527-1/-2 | ||
| Elongation at Break | 2.5 % | 2.5 % | ISO 527-1/-2 | ||
| Tensile Modulus | 12.0 GPa | 1740 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 5.00 J/cm2 @Temperature -30.0 °C | 23.8 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | ||
| 5.00 J/cm2 @Temperature 23.0 °C | 23.8 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.900 J/cm2 @Temperature -30.0 °C | 4.28 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.00 J/cm2 @Temperature 23.0 °C | 4.76 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 4.0 @Frequency 1e+6 Hz | 4.0 @Frequency 1e+6 Hz | IEC 60250 | ||
| 4.3 @Frequency 100 Hz | 4.3 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.00060 @Frequency 100 Hz | 0.00060 @Frequency 100 Hz | IEC 60250 | ||
| 0.0016 @Frequency 1e+6 Hz | 0.0016 @Frequency 1e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 225 V | 225 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 μm/m-°C @Temperature 20.0 °C | 11.1 μin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 80.0 μm/m-°C @Temperature 20.0 °C | 44.4 μin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| Melting Point | 295 °C | 563 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 290 °C | 554 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 290 °C | 554 °F | 50°C/h 50N; ISO 306 | ||
| Glass Transition Temp, Tg | 75.0 °C | 167 °F | Glass Transition Temperature (10°C/min); ISO 11357-1/-2 | ||
| UL RTI, Electrical | 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | UL746B | ||
| 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | UL746B | |||
| UL RTI, Mechanical with Impact | 110 °C @Thickness 0.750 mm | 230 °F @Thickness 0.0295 in | UL746B | ||
| 125 °C @Thickness 1.50 mm | 257 °F @Thickness 0.0591 in | UL746B | |||
| UL RTI, Mechanical without Impact | 120 °C @Thickness 0.750 mm | 248 °F @Thickness 0.0295 in | UL746B | ||
| 125 °C @Thickness 1.50 mm | 257 °F @Thickness 0.0591 in | UL746B | |||
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | IEC 60695-11-10 | ||
| V-0 @Thickness 0.350 mm | V-0 @Thickness 0.0138 in | IEC 60695-11-10 | |||
| Oxygen Index | 37 % | 37 % | ISO 4589-1/-2 | ||
| Glow Wire Test | 825 °C @Thickness 0.750 mm | 1520 °F @Thickness 0.0295 in | Glow Wire Ignition Temperature; IEC 60695-2-13 | ||
| 850 °C @Thickness 3.00 mm | 1560 °F @Thickness 0.118 in | Glow Wire Ignition Temperature; IEC 60695-2-13 | |||
| 960 °C @Thickness 0.750 mm | 1760 °F @Thickness 0.0295 in | Glow Wire Flammability Index; IEC 60695-2-12 | |||
| 960 °C @Thickness 3.00 mm | 1760 °F @Thickness 0.118 in | Glow Wire Flammability Index; IEC 60695-2-12 | |||
| Descriptive Properties | |||||
| Flame Retardant | Yes | ||||
| Flame Retarding Agent | Yes | ||||
| Heat Stabilized or Stable to Heat | Yes | ||||
| Injection Molding | Yes | ||||
| Lubricants | Yes | ||||
| Platable | Yes | ||||
| Release Agent | Yes | ||||
| With Fillers | Yes | ||||