- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 1.6
- 缺口沖擊強度: 2.67
- 拉伸強度 [MPa]: 68.9
- 斷裂伸長率 [%]: 96.5
- 彎曲模量 [MPa]: 2.65
- 硬度: 114.0
- 熱變形溫度 [℃]: 216.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | ASTM D792 |
| Water Absorption | 1.6 % @Time 86400 sec | 1.6 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm @Thickness 3.17 mm | 0.015 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 114 | 114 | ASTM D785 |
| Tensile Strength, Yield | 68.9 MPa | 10000 psi | ASTM D638 |
| Elongation at Break | 80 % | 80 % | ASTM D638 |
| Flexural Yield Strength | 96.5 MPa | 14000 psi | ASTM D790 |
| Flexural Modulus | 2.65 GPa | 385 ksi | ASTM D790 |
| Izod Impact, Notched | 2.67 J/cm @Thickness 3.17 mm | 5.00 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 17.3 kV/mm | 440 kV/in | Method A (Short-Time); ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 86.4 μm/m-°C | 48.0 μin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 420 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.1 °C | 160 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |