- 密度 [g/cm3]: 1.5
- 缺口沖擊強度: 8.5
- 彎曲模量 [MPa]: 11.6
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in3 | ISO 1183-87 |
| Filler Content | 43 % | 43 % | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ISO DIS 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.011 cm/cm | 0.0070 - 0.011 in/in | ISO DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 160 MPa | 23200 psi | ISO 527-93 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-93 |
| Flexural Strength | 235 MPa | 34100 psi | ISO 178-93 |
| Flexural Modulus | 11.6 GPa | 1680 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 8.50 kJ/m2 | 4.04 ft-lb/in2 | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ISO 75-93 |