- 密度 [g/cm3]: 1.7
- 吸水率 [%]: 0.35
- 缺口沖擊強度: 1.87
- 拉伸強度 [MPa]: 241.0
- 斷裂伸長率 [%]: 352
- 彎曲模量 [MPa]: 1.76
- 硬度: 121.0
- 熱變形溫度 [℃]: 257.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in3 | ASTM D792 |
| Water Absorption | 0.35 % @Time 86400 sec | 0.35 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 3.17 mm | 0.0030 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength, Yield | 241 MPa | 35000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 352 MPa | 51000 psi | ASTM D790 |
| Flexural Modulus | 1.76 GPa | 255 ksi | ASTM D790 |
| Izod Impact, Notched | 1.87 J/cm @Thickness 3.17 mm | 3.50 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 18.9 kV/mm | 480 kV/in | Method A (Short-Time); ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 12.6 μm/m-°C | 7.00 μin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 241 °C | 465 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |